Repair Ceramic Composite Compounds

MAXWELD offers a whole range of Resin Coposites including Metal Repair and Rebuilding, Erossion corrosion Protection, Abrasion resistant linings, Wether and waterproofing, High temperature coatings, Corrosion protection, Concrete repair and protection, Safety Grip Systems, used in many different industrial applicacions. Those resin composite systems provide excellent resistance against aggressive liquid solid and gas media flow, corrosion, abrasion, cavitation, erosion, aggressive chemicals. This range of products extends life even 10-fold used in pumps impellers, tanks, heat exchangers, chutes, landings, columns, chimneys, steel and concrete constructions, marine applications, etc...

MC-2501
MAXWELD® CP01 - E METAL RAPID
Fast cure Metal Repair Compound. (5 min). Fast repairs, filling cavities, leaks, etc. Temperature service: (-50°C ÷ 120°C, short 170°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
1.3 : 1
1 : 1
Density [kg/dm3]
2.2
Minimal thickness of 1 layer
2 mm
Open time
2 min
Initial strength time
5 min
Funcional strength time
30 min
Time to Another layer application
10 min
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 120/170
MC-2502
MAXWELD® CP02 - SUPER METAL
Metalic Repair Compound. Super Metal. (30min). Rebuilding shape, filling holes, cavities in mechanical parts, shaft, pumps, etc. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
5.67 : 1
4 : 1
Density [kg/dm3]
2.44
Minimal thickness of 1 layer
2 mm
Open time
15 min
Initial strength time
30 min
Funcional strength time
2 h
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200/230
MC-2502A
MAXWELD® CP02A - SUPER ALUMINIUM
Aluminium Metallic Paste. Super Aluminum. (30 minutes). Rebuilding the shape, filling the cavities. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
2.4 : 1
Density [kg/dm3]
1.80
Minimal thickness of 1 layer
2 mm
Open time
15 min
Initial strength time
30 min
Funcional strength time
2 h
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2502B
MAXWELD® CP02B - SUPER BRONZE
Bronze filled Metal Paste. (30min). Rebuilding shape, filling cavities and leaks. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
8.75 : 1
Density [kg/dm3]
2.90
Minimal thickness of 1 layer
2 mm
Open time
15 min
Initial strength time
30 min
Funcional strength time
2 h
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2502R
MAXWELD® CP02R - SUPER BRASS
Brass filled Metalic Paste. (30min). Rebuilding shape, filling cavities and leaks. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
4.3 : 1
Density [kg/dm3]
2.10
Minimal thickness of 1 layer
2 mm
Open time
15 min
Initial strength time
30 min
Funcional strength time
2 h
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2502T
MAXWELD® CP02T - SUPER TYTANIUM
Tytanium filled Metallic Paste. (30 minutes). Rebuilding the shape, replenishing the cavities. Temperature service: (-50°C÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
4 : 1
Density [kg/dm3]
2.0
Minimal thickness of 1 layer
2 mm
Open time
15 min
Initial strength time
30 min
Funcional strength time
2 h
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2503
MAXWELD® CP03 - SUPER XL METAL
Slow cure Metal Compound. Super Metal. (3 h). Recommended for large cavities and holes. Rebuilding shape of large parts. Machining possible after 4 hours from application time. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
6.25 : 1
5 : 1
Density [kg/dm3]
2.44
Minimal thickness of 1 layer
2 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2504
MAXWELD® CP04 - CERAMIC R METAL
Ceramic Paste Repair Compound. (30 min). Extra abrasion and cavitation resistance. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
5.67 : 1
4 : 1
Density [kg/dm3]
2.32
Minimal thickness of 1 layer
2 mm
Open time
15 min
Initial strength time
30 min
Funcional strength time
2 h
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2505
MAXWELD® CP05 - CERAMIC R XL METAL
Slow cure Ceramic Paste Repair Compound. (3 h). Extra abrasion and cavitation resistance. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
6.25 : 1
5 : 1
Density [kg/dm3]
2.38
Minimal thickness of 1 layer
2 mm
Open time
30min
Initial strength time
3 h
Funcional strength time
2 h
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2506
MAXWELD® CP06 - CERAMIC S METAL
Fluid Ceramic Coating Repair Compound. (30 min). Extra abrasion, turbulent media flows and cavitation resistance, pump impereller. 1 layer coating thickness is minimum 0.35 mm. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
11.52 : 1
Density [kg/dm3]
2.15
Minimal thickness of 1 layer
0.35 mm
Open time
15 min
Initial strength time
30 min
Funcional strength time
2 h
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2507
MAXWELD® CP07 - CERAMIC S XL METAL
Slow Cure Fluid Ceramic Coating Repair Compound. (3 h). Extra abrasion, turbulent media flows and cavitation resistance, pump impereller. 1 layer coating thickness is minimum 0.35 mm. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
15.55 :1
Density [kg/dm3]
2.15
Minimal thickness of 1 layer
0.35 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2508
MAXWELD® CP08 - XL FLUID METAL
Liquid Slow Cure Fluid Ceramic Coating Repair Compound. (3h). Liquid penetrating in cracks and gap filler of 0.2-0.5mm. Extra abrasion, turbulent media flows and cavitation resistance, pump impereller. 1 layer coating thickness is minimum 0.25 mm. Bonding of different materials. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
9.3 : 1
Density [kg/dm3]
1.8
Minimal thickness of 1 layer
0.25 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2509
MAXWELD® CP09 - CERAMIC F GLIDE
Fast, Special Glide Fluid Ceramic Coating Repair Compound. (10 min). Extra slippery properties for easy media flow, abrasion, turbulent media flows and cavitation resistance, pump imperellers nad cases. Increases up to 20% of pump efficiency. 1 layer coating thickness is minimum 0.15-0.20 mm. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
3.64 : 1
Density [kg/dm3]
1.8
Minimal thickness of 1 layer
0.15 mm
Open time
5 min
Initial strength time
10 min
Funcional strength time
40 min
Time to Another layer application
10 min
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2510
MAXWELD® CP10 - CERAMIC F XL GLIDE
Slow Cure Special Glide Fluid Ceramic Coating Repair Compound. (10 min). Extra slippery properties for easy media flow, abrasion, turbulent media flows and cavitation resistance, pump imperellers nad cases. Increases up to 12% of pump efficiency. 1 layer coating thickness is minimum 0.15-0.20 mm. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
10.29 : 1
Density [kg/dm3]
2.1
Minimal thickness of 1 layer
0.25mm
Open time
60 min
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2511
MAXWELD® CP11 - METAL T SLIDE
Metal Glide Paste. (30 min). Good slippery properties. For repair of slides, actuators, shafts for orings assembly, pins, etc. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
5.6 :1
Density [kg/dm3]
2,44
Minimal thickness of 1 layer
0.25mm
Open time
15 min
Initial strength time
30 min
Funcional strength time
2 h
Time to Another layer application
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2512
MAXWELD® CP12 - METAL F SLIDE
Slow Cure Fluid Metal Repair Compound. (3 h). Coating with good slippery properties. 1 layer coating thickness is minimum 0.35mm. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
11.2 :1
Density [kg/dm3]
1.9
Minimal thickness of 1 layer
0.35mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2513
MAXWELD® CP13 - CERAMIC 60
Special Cermic Fluid Paste with special abrasion resistance fillers. (3 h). Very resistant to abrasion, cavitation, turbulent abrasive media flows. Minimum thickness of 1 layer is 1mm. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
14.52 : 1
Density [kg/dm3]
2.2
Minimal thickness of 1 layer
1 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2514
MAXWELD® CP14 - CERAMIC CARBIDE 24
Special Ceramic Paste Repair Compound (3 h) with higher minimum thickness of 1.5-2mm. Recommended for large holes or as thick layers resistant to abrasion, shock, cavities in pipes, mixers and other heavuly loaded equipment. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
7.2 : 1
Density [kg/dm3]
2.46
Minimal thickness of 1 layer
2 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2515
MAXWELD® CP15 - CERAMIC CARBIDE 13
Special Ceramic Paste Repair Compound (3 h) with much higher minimum thickness of 5-6 mm. Recommended for large holes or as thick layers resistant to abrasion, heavy shocks, cavities in pipes, skids, mixers and other heavuly loaded equipment. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
6.21 : 1
Density [kg/dm3]
2.48
Minimal thickness of 1 layer
6 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2516
MAXWELD® CP16 - CERAMIC K 3-4
Special Ceramic Paste Repair Compound (3 h) with higher minimum thickness of 6mm. Recommended as a layer agains abrasion where haevy shocks takes place, against wood chips, sand, gravel in pipe elbows, mixers and other heavily loaded equipment. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
8.8 : 1
Density [kg/dm3]
2.6
Minimal thickness of 1 layer
6 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
5 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2517
MAXWELD® CP17 - RUBBER POLYMER
Flexible Ceramic Coating Repair Compound (30 min) for filling holes in rubber coatings, flexible coating on flexible metals. Resistant to shocks, abrasion and chemical attack. 1 layer minimum thickness. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
1.6 : 1
2 : 1
Density [kg/dm3]
1.6
Minimal thickness of 1 layer
0.5 mm
Open time
15 min
Initial strength time
30 min
Funcional strength time
4 h
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2518
MAXWELD® CP18 - RUBBER XL POLYMER
Slow Cure Flexible Ceramic Coating Repair Compound (3h) for filling holes in rubber coatings, flexible coating on flexible metals. Resistant to shocks, abrasion and chemical attack. 1 layer minimum thickness. Temperature service: (-50°C÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
1.6 : 1
2 : 1
Density [kg/dm3]
1,6
Minimal thickness of 1 layer
0.5 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
45h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2519
MAXWELD® CP19 - PAINT-EXTREME
Fluid Ceramic Coating Repair Compound (15 min) Flexible paint protecting against rust, corrosion and aggresive media. For pump cases, construction structurers made of concrete and steel. Available colours: Grey, Black, Red, orange. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
3 : 1
Density [kg/dm3]
1,4
Minimal thickness of 1 layer
0.15 mm
Open time
15 min
Initial strength time
5 h
Funcional strength time
7 h
Time to Another layer application
12 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2520
MAXWELD® CP20 - CERQUARTZ
Ceramic Quarz Floor Repair Paste Compound (2 h) Concreate floor epoxy repair compound resistant to aggresive media and heavy load. The repaired floor can used within 4 hours (forklifts). Protection of floors, fundations, dilatations, etc. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
4 : 1
3 : 1
Density [kg/dm3]
2.1
Minimal thickness of 1 layer
2 mm
Open time
15 min
Initial strength time
2 h
Funcional strength time
4 h
Time to Another layer application
3 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2521
MAXWELD® CP21 - CERQUARTZ-F
Fluid Ceramic Quarz Floor Coating Compound (2 h). Concreate floor epoxy repair coating resistant to aggresive media and heavy load. The repaired floor can used within 4 hours (forklifts). Protection of floors, fundations, dilatations, etc. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
6 : 1
Density [kg/dm3]
1.9
Minimal thickness of 1 layer
0.25 mm
Open time
15 min
Initial strength time
2 h
Funcional strength time
4 h
Time to Another layer application
3 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2522
MAXWELD® CP22 - CERQUARTZ RAPID
Fast Cure Ceramic Quarz Floor Repair Paste Compound (30min) Concreate floor epoxy repair compound resistant to aggresive media and heavy load. The repaired floor can used within 30 min. (forklifts). Protection of floors, fundations, dilatations, etc. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
2 : 1
2 : 1
Density [kg/dm3]
2
Minimal thickness of 1 layer
2 mm
Open time
10 min
Initial strength time
1 h
Funcional strength time
30 min
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2523
MAXWELD® CP23 - CERQUARTZ-F RAPID
Fast Cure Fluid Ceramic Quarz Floor Coating Compound (30 min). Concreate floor epoxy repair coating resistant to aggresive media and heavy load. The repaired floor can used within 4 hours (forklifts). Protection of floors, fundations, dilatations, etc. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
1.3 : 1
Density [kg/dm3]
1.6
Minimal thickness of 1 layer
0.25 mm
Open time
10 min
Initial strength time
1 h
Funcional strength time
30 min
Time to Another layer application
2 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2530
MAXWELD® CP30 - SUPER METAL XHT
High Temperature Metalic Repair Compound. Super Metal. (3h). Rebuilding shape, filling holes, cavities in mechanical parts, shaft, pumps, etc. Temperature service: (-50°C ÷ 230°C, short 270°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
5.67 : 1
Density [kg/dm3]
2.44
Minimal thickness of 1 layer
2 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
45h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 230 /270
MC-2533
MAXWELD® CP33 - CERAMIC HTG
Special Antiadhesive Slow Cure Ceramic Coating Repair Compound (6h) recommended as a finish coating of shafts, cylinders used in paper machines. It is anti-adhesive to wet pulp and paper. Temperature service: (-50°C ÷ 230°C, short 270°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
12:1
Density [kg/dm3]
1.8
Minimal thickness of 1 layer
0.5 mm
Open time
120 min.
Initial strength time
6 h
Funcional strength time
24h
Time to Another layer application
3 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2540
MAXWELD® CP40 - CLEAN-X
Fast evaporating solvent degreaser. Drying Time <1 min. Used before the application of MAXWELD® Ceramic Repair Compounds.
Packaging
1L, 5L, 25L
Mix [weight] [vol.]
Density [kg/dm3]
Minimal thickness of 1 layer
Open time
1 min
Initial strength time
Funcional strength time
Time to Another layer application
Mechanical strength
Full chemical strength
Working Temperature range [˚C]
MC-2541
MAXWELD® CP41 - PRIMER
Primer used on concrete floors before the application of Ceramic coatings like CERQUARTZ-F, CERQUARTZ, CERQUARTZ-F RAPID. Cure time 60 min. @ 20°C.
Packaging
1L, 5L, 25L
Mix [weight] [vol.]
Density [kg/dm3]
1.2
Minimal thickness of 1 layer
0.1 mm
Open time
20 min.
Initial strength time
Funcional strength time
40 min
Time to Another layer application
Mechanical strength
60 min
Full chemical strength
Working Temperature range [˚C]
MC-2525
MAXWELD® CP25 - ABRAS CERAMIC 24
Flexible Extra Shock Resistant Ceramic Paste Repair Compound (3 h). Special extra shock resistance thanks to is shock absorbtion abilities. Resistant to agressive media and abrasive mieda flows. 1 layer minimum thicknes 1.5-2mm. Recommende for large holes, pipe bent, elbows, gravel media, sand. Temperature service: (-50°C ÷ 200°C, short 230°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
6.5 : 1
Density [kg/dm3]
2.25
Minimal thickness of 1 layer
1.5 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
3 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 200 /230
MC-2551
MAXWELD® CP51 - CERAMIC S XL METAL HT
High temperature Ceramic Repair Coating. Fluid ceramic coating (3 h). 1 layer minimum thickness 0.35 mm. Resistant to extreme abrasion and high temperatures dry and wet. Temperature service: (-50°C ÷ 230°C, short 270°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
18.66 :1
Density [kg/dm3]
2.15
Minimal thickness of 1 layer
0.35 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 230 /270
MC-2552
MAXWELD® CP52 - CERAMIC 60 HT
High temperature Ceramic Repair Coating. Fluid ceramic coating (3 h). 1 layer minimum thickness 1 mm. Resistant to extreme abrasion and high temperatures dry and wet. Temperature service: (-50°C ÷ 230°C, short 270°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
14.52 : 1
Density [kg/dm3]
2.2
Minimal thickness of 1 layer
1 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 230 /270
MC-2553
MAXWELD® CP53 - CERAMIC CARBIDE 24 HT
High temperature Ceramic Repair Paste Compound. Ceramic Paste (3 h). 1 layer minimum thickness 2 mm. Resistant to extreme abrasion and high temperatures dry and wet. In case of extreme shocks recommended minium thickness 20mm. Temperature service: (-50°C ÷ 230°C, short 270°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
7.2 : 1
Density [kg/dm3]
2.46
Minimal thickness of 1 layer
2 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 230 /270
MC-2556
MAXWELD® CP56 - CERAMIC CARBIDE 13 HT
High temperature Ceramic Repair Paste Compound. Ceramic Paste (3 h). 1 layer minimum thickness 5-6 mm. Resistant to extreme abrasion and high temperatures dry and wet. In case of extreme shocks recommended minium thickness 20mm. Temperature service: (-50°C ÷ 230°C, short 270°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
6.21 : 1
Density [kg/dm3]
2.48
Minimal thickness of 1 layer
6 mm
Open time
30 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 230 /270
MC-2557
MAXWELD® CP57 - CERAMIC CARBIDE 35 HT
High temperature Ceramic Repair Paste Compound. Ceramic Paste (3 h). 1 layer minimum thickness 6 mm. Resistant to extreme abrasion and high temperatures dry and wet. In case of extreme shocks recommended minium thickness 20mm. For repair and protection of pump, gravel and coal skids, pipe elbows, mixer blades. Temperature service: (-50°C ÷ 230°C, short 270°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
8 : 1
Density [kg/dm3]
2.70
Minimal thickness of 1 layer
1 mm
Open time
45 min.
Initial strength time
3 h
Funcional strength time
4 h
Time to Another layer application
4 h
Mechanical strength
24 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 230 /270
MC-2571
MAXWELD® CP71 - CERAMIC SHT
Ultra High temperature Ceramic Repair Coating Compound. Ceramic Fluid (3 h). 1 layer minimum thickness 0.5-1mm. Resistant to extreme abrasion and high temperatures only in dry environment. Temperature service: (-50°C ÷ 600°C, short 900°C)
Packaging
500g, 1kg, 5kg
Mix [weight] [vol.]
1 : 1
Density [kg/dm3]
Minimal thickness of 1 layer
0.5-1 mm
Open time
1 h.
Initial strength time
24 h
Funcional strength time
48 h
Time to Another layer application
48 h
Mechanical strength
48 h
Full chemical strength
7 days
Working Temperature range [˚C]
-50 ÷ 600 /900