Methacrylate Adhesives

MAXWELD® strukctural adhesives is a full range of high performance two parts methacrylate adhesives for bonding metals, plastics, composites without rivets, welding, screws and laminating.
MAXWELD® Methyl Methacrylate Adhesives are commonly used as structural adhesives due to their excellent strength, impact resistance, thermal shock, fatigue resistance, peel strength and chemical resistance.
They are based on thermoset adhesives formulations that give excellent structural properties to bond a wide - variety of durable substrates widely used in transportation vehicles manufacturing (cars, trucks, buses, railway, yachts, aerospace)
Following is the list of standard grades and packaging available and we also custom formulations and packaging based on customer requirement.
MAXWELD® MMAs` can withstand paint bake cycles, including powder coating and electron coating, at typically 230°C for up to 45 minutes with no loss of strength.
The differences in viscosity, pot life and cure times enables manufacturers to choose the optimal solution that best suit their production processes.

MAXWELD® - METHACRYLATE ADHESIVES 1:1

MC-2661
M20
Structural Adhesive primerless bond system for metal composite and thermoplastic subtrates. 5-7 Minute Open time, 12-15 minute handling strength, Non Slump 1:1 Structural (Standard/Black). Excellent on steel, stainless steel, Aluminium, galvanized steel and all composites.
Size
25ml, 50ml, 400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Cream, Black
Min. Open Time [Minutes]
4
Max. Open Time [Minutes]
7
Min. Handling Strength [Minutes]
13
Max. Handling Strength [Minutes]
15
Max Gap Fill: [mm]
5
Approx Viscosity [cP]
450000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
4350
21/38/32
Min. Tensile Elongation (%)
10
Max. Tensile Elongation (%)
15
Temperature Range [˚C]
-55 ÷ 150 (220)
MC-2602
MPG-8
Fast setting structural adhesive, low viscosity for a very wide range of substrates: metals, plstics, composites, glas, wood. Transparent on glass-metal bond. Mix or no-mix applications.
Size
25ml, 50ml, 400ml & Bulk
Mix Ratio
1 : 1
Colour
Różowy & Zielony = Transparent
Min. Open Time [Minutes]
2
Max. Open Time [Minutes]
3
Min. Handling Strength [Minutes]
4
Max. Handling Strength [Minutes]
8
Max Gap Fill: [mm]
1
Approx Viscosity [cP]
4000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
30
Min. Tensile Elongation (%)
5
Max. Tensile Elongation (%)
10
Temperature Range [˚C]
-55 ÷ 121 (200)
MC-2431 / MC-2431B / MC-2431W
MB-15 / MB-15B / MB-15W
High performance, General purpose, Structural Adhesive to bond metal composite and thermoplastic subtrates. 4-6 Minute Open time Non Slump 1:1 Structural (Standard/Black). Complies with EN45 545 and Cataplasma test DVS 1618 in Rail manufacturing process.
Size
25ml, 50ml, 400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Cream, Black, Grey, White
Min. Open Time [Minutes]
4
Max. Open Time [Minutes]
6
Min. Handling Strength [Minutes]
12
Max. Handling Strength [Minutes]
15
Max Gap Fill: [mm]
4
Approx Viscosity [cP]
60000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3850
26.5
Min. Tensile Elongation (%)
20
Max. Tensile Elongation (%)
30
Temperature Range [˚C]
-55 ÷ 121 (230)
MC-2432 / MC-2432B / MC-2432W
MB-35 / MB-35B / MB-35W
General purpose, Structural Adhesive to bond metal composite and thermoplastic subtrates. 14-16 Minute Open time Non Slump 1:1 Structural (Standard/Black). Complies with EN45 545 and Cataplasma test DVS 1618 in Rail manufacturing process.
Size
25ml, 50ml, 400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Cream, Black, Grey, White
Min. Open Time [Minutes]
15
Max. Open Time [Minutes]
18
Min. Handling Strength [Minutes]
30
Max. Handling Strength [Minutes]
35
Max Gap Fill: [mm]
4
Approx Viscosity [cP]
60000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3850
26.5
Min. Tensile Elongation (%)
7
Max. Tensile Elongation (%)
18
Temperature Range [˚C]
-55 ÷ 121 (230)
MC-2430
MB-8
Fast Curing Automotive Grade. 3-4 min open time 6-8 min cure high strength non slump 1:1 structural adhesive (Standard/Black). Complies with EN45 545 and Cataplasma test DVS 1618 in Rail manufacturing process.
Size
25ml, 50ml, 400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Cream, Black
Min. Open Time [Minutes]
2
Max. Open Time [Minutes]
3
Min. Handling Strength [Minutes]
6
Max. Handling Strength [Minutes]
9
Max Gap Fill: [mm]
4
Approx Viscosity [cP]
60000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3500
24
Min. Tensile Elongation (%)
15
Max. Tensile Elongation (%)
27
Temperature Range [˚C]
-55 ÷ 121 (230)
MC-2433
MB-75
Long open time 25-30 min. High performance adhesive with excellent adhesion to wide variety of metal and plastic surfaces
Size
50ml, 400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Yellow
Min. Open Time [Minutes]
25
Max. Open Time [Minutes]
30
Min. Handling Strength [Minutes]
60
Max. Handling Strength [Minutes]
75
Max Gap Fill: [mm]
4
Approx Viscosity [cP]
60000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
9
Max. Tensile Elongation (%)
20
Temperature Range [˚C]
-55 ÷ 121 (230)
MC-2434
MB-120
All purpose adhesive with high toughness and long open time.
Size
50ml, 400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Yellow
Min. Open Time [Minutes]
40
Max. Open Time [Minutes]
45
Min. Handling Strength [Minutes]
90
Max. Handling Strength [Minutes]
120
Max Gap Fill: [mm]
4
Approx Viscosity [cP]
60000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3500
24
Min. Tensile Elongation (%)
40
Max. Tensile Elongation (%)
45
Temperature Range [˚C]
-55 ÷ 121 (230)
MC-2435
MW-15
UV stable, Ultra white adhesive to bond variety of plastics, cellular PVC, composites and metals. Excellent water resistance properties for MARINE applications.
Size
50ml, 400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Ultra White
Min. Open Time [Minutes]
4
Max. Open Time [Minutes]
6
Min. Handling Strength [Minutes]
12
Max. Handling Strength [Minutes]
16
Max Gap Fill: [mm]
1
Approx Viscosity [cP]
90000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3850
26.5
Min. Tensile Elongation (%)
3
Max. Tensile Elongation (%)
6
Temperature Range [˚C]
-55 ÷ 121
MC-2436
MW-30
UV stable, Ultra white adhesive to bond variety of plastics, composites and metals.
Size
400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Ultra White
Min. Open Time [Minutes]
6
Max. Open Time [Minutes]
9
Min. Handling Strength [Minutes]
22
Max. Handling Strength [Minutes]
28
Max Gap Fill: [mm]
4
Approx Viscosity [cP]
60000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3850
26.5
Min. Tensile Elongation (%)
7
Max. Tensile Elongation (%)
18
Temperature Range [˚C]
-55 ÷ 121
MC-2437
MB-275
All purpose adhesive with extra long open time 120-130 min.
Size
50ml, 400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Cream, White
Min. Open Time [Minutes]
120
Max. Open Time [Minutes]
130
Min. Handling Strength [Minutes]
260
Max. Handling Strength [Minutes]
275
Max Gap Fill: [mm]
4
Approx Viscosity [cP]
60000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3850
26.5
Min. Tensile Elongation (%)
55
Max. Tensile Elongation (%)
65
Temperature Range [˚C]
-55 ÷ 121
MC-2420
MR-175
High viscosity MARINE adhesive with long open time 70-75 min.
Size
400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Cream, Black
Min. Open Time [Minutes]
70
Max. Open Time [Minutes]
75
Min. Handling Strength [Minutes]
150
Max. Handling Strength [Minutes]
175
Max Gap Fill: [mm]
4
Approx Viscosity [cP]
200000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3850
26.5
Min. Tensile Elongation (%)
50
Max. Tensile Elongation (%)
60
Temperature Range [˚C]
-55 ÷ 121
MC-2421
MR-225
Long open time 95 min. high viscosity MARINE adhesive for extra large components and large gaps.
Size
400ml, 18kg, 182 kg
Mix Ratio
1 : 1
Colour
Cream, Black, White
Min. Open Time [Minutes]
90
Max. Open Time [Minutes]
95
Min. Handling Strength [Minutes]
190
Max. Handling Strength [Minutes]
225
Max Gap Fill: [mm]
4
Approx Viscosity [cP]
200000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
55
Max. Tensile Elongation (%)
65
Temperature Range [˚C]
-55 ÷ 121

TRANSPARENT MMA`S

MC-2877
MT-G5
Clear structural adhesive for clear bonding acrylics, displays, plexi PMMA. Resistant to Cataplasma ageing test DVS 1618
Size
50ml
Mix Ratio
1 : 1
Colour
Transparent
Min. Open Time [Minutes]
2
Max. Open Time [Minutes]
3
Min. Handling Strength [Minutes]
5
Max. Handling Strength [Minutes]
10
Max Gap Fill: [mm]
1
Approx Viscosity [cP]
7500
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
1750
12
Min. Tensile Elongation (%)
3
Max. Tensile Elongation (%)
5
Temperature Range [˚C]
-55 ÷ 121
MC-2410
MTX-15
Clear adhesive for clear bonding plastics, acrylics, Plexi PMMA, Polycarbonate, PET, ABS metals with medium cure speed, 12-16 open time. Widely used for sign, display, electronics, large components and many other industrial bonding applications.
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
Transparent
Min. Open Time [Minutes]
6
Max. Open Time [Minutes]
8
Min. Handling Strength [Minutes]
12
Max. Handling Strength [Minutes]
14
Max Gap Fill: [mm]
1
Approx Viscosity [cP]
12000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
1750
12
Min. Tensile Elongation (%)
3
Max. Tensile Elongation (%)
5
Temperature Range [˚C]
-55 ÷ 121

MAXWELD® - METHACRYLATE ADHESIVES 10:1

MC-2407
MHT-20
High Temperature, high performance adhesive with fast curing time. High toughness and strength with excellent resistance properties. Suitable for use before high temperature powder coating process 220°C @30 min.
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
Black
Min. Open Time [Minutes]
4
Max. Open Time [Minutes]
6
Min. Handling Strength [Minutes]
15
Max. Handling Strength [Minutes]
18
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
120000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
45
Max. Tensile Elongation (%)
45
Temperature Range [˚C]
-55 ÷ 121 (230)
MC-2401
MWX-2
Extremely fast cure speed, 30 sec. Open time, general purpose adhesive. High adhesion to most metals and plastics. Horse Shoe bonding.
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
White
Min. Open Time [Minutes]
25 sec.
Max. Open Time [Minutes]
35 sec.
Min. Handling Strength [Minutes]
1
Max. Handling Strength [Minutes]
2
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
120000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3750
<30
Min. Tensile Elongation (%)
55
Max. Tensile Elongation (%)
75
Temperature Range [˚C]
-55 ÷ 121
MC-2402
MFX-32
Flexible adhesive with excellent low temperature properties, toughness and strength.
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
Cream, Blue, Black
Min. Open Time [Minutes]
8
Max. Open Time [Minutes]
15
Min. Handling Strength [Minutes]
25
Max. Handling Strength [Minutes]
32
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
120000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
110
Max. Tensile Elongation (%)
145
Temperature Range [˚C]
-55 ÷ 121
MC-2403
MPX-9
Adhesive with fast cure speed, 2-3 min. open time. Flexible with an excellent toughness and strength. Caravan panel bonding, Fieber glass, ABS, Metala
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
Cream, Blue, Black
Min. Open Time [Minutes]
2
Max. Open Time [Minutes]
3
Min. Handling Strength [Minutes]
6
Max. Handling Strength [Minutes]
9
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
175000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
105
Max. Tensile Elongation (%)
105
Temperature Range [˚C]
-55 ÷ 121
MC-2404
MPX-20
High performance adhesive with fast curing time, 4-6 min. open time. Flexible with High toughness and strength with excellent resistance properties. Suitable for powder coating.
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
Cream, Blue, Black
Min. Open Time [Minutes]
4
Max. Open Time [Minutes]
6
Min. Handling Strength [Minutes]
15
Max. Handling Strength [Minutes]
18
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
125000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
135
Max. Tensile Elongation (%)
135
Temperature Range [˚C]
-55 ÷ 121
MC-2405
MPX-40
High performance with medium cure speed, 17-22 min. open time. Flexible with high strength. Excellent adhesion to wide variety of plastic composites and metal surfaces.
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
Cream, Blue, Black
Min. Open Time [Minutes]
17
Max. Open Time [Minutes]
22
Min. Handling Strength [Minutes]
35
Max. Handling Strength [Minutes]
40
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
125000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
105
Max. Tensile Elongation (%)
105
Temperature Range [˚C]
-55 ÷ 121
MC-2406
MPX-90
High performance with long cure speed, 30-35 min. open time. Flexible with high strength. Excellent adhesion to wide variety of plastic composites and metal surfaces.
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
Cream, Blue, Black
Min. Open Time [Minutes]
30
Max. Open Time [Minutes]
35
Min. Handling Strength [Minutes]
80
Max. Handling Strength [Minutes]
90
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
125000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
130
Max. Tensile Elongation (%)
130
Temperature Range [˚C]
-55 ÷ 121
MC-2408
MWX-60
Ultra White colour adhesive with medium cure speed, 18-22 min. open time. Low shrinkage with excellent adhesion to wide variety of surfaces.
Size
490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
White
Min. Open Time [Minutes]
18
Max. Open Time [Minutes]
22
Min. Handling Strength [Minutes]
45
Max. Handling Strength [Minutes]
60
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
125000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
60
Max. Tensile Elongation (%)
70
Temperature Range [˚C]
-55 ÷ 121
MC-2429
MRX-80
UV stable, white colour adhesive for MARINE applications. Long cure speed, 40-45 open time. High toughness.
Size
490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
White
Min. Open Time [Minutes]
40
Max. Open Time [Minutes]
45
Min. Handling Strength [Minutes]
70
Max. Handling Strength [Minutes]
80
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
165000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
55
Max. Tensile Elongation (%)
65
Temperature Range [˚C]
-55 ÷ 121
MC-2428
MRX-175
High viscosity MARINE adhesive with long open time, 70-75 min.
Size
18kg, 182kg
Mix Ratio
10 : 1
Colour
Cream
Min. Open Time [Minutes]
70
Max. Open Time [Minutes]
75
Min. Handling Strength [Minutes]
150
Max. Handling Strength [Minutes]
175
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
165000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
125
Max. Tensile Elongation (%)
150
Temperature Range [˚C]
-55 ÷ 121
MC-2427
MRX-360
High viscosity MARINE adhesive with extra long open time, 90-120 min.
Size
18kg, 182kg
Mix Ratio
10 : 1
Colour
Cream
Min. Open Time [Minutes]
90
Max. Open Time [Minutes]
120
Min. Handling Strength [Minutes]
190
Max. Handling Strength [Minutes]
360
Max Gap Fill: [mm]
10
Approx Viscosity [cP]
165000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3200
22
Min. Tensile Elongation (%)
130
Max. Tensile Elongation (%)
180
Temperature Range [˚C]
-55 ÷ 121
MC-2411
MMX-20
Special adhesive for primerless metal bonding and fast cure speed, 4-6 min. open time. High toughness and strength with excellent resistance properties.
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
Grey
Min. Open Time [Minutes]
4
Max. Open Time [Minutes]
6
Min. Handling Strength [Minutes]
15
Max. Handling Strength [Minutes]
18
Max Gap Fill: [mm]
2
Approx Viscosity [cP]
125000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3750
<30
Min. Tensile Elongation (%)
35
Max. Tensile Elongation (%)
40
Temperature Range [˚C]
-55 ÷ 121
MC-2412
MMX-40
Special adhesive for primerless metal bonding and medium cure speed, 12-18 min. open time. High toughness and strength with excellent resistance properties.
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
Grey
Min. Open Time [Minutes]
12
Max. Open Time [Minutes]
18
Min. Handling Strength [Minutes]
35
Max. Handling Strength [Minutes]
40
Max Gap Fill: [mm]
1
Approx Viscosity [cP]
125000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
3750
<30
Min. Tensile Elongation (%)
35
Max. Tensile Elongation (%)
45
Temperature Range [˚C]
-55 ÷ 121
MC-2400
MPP-120
Special adhesive for bonding difficult to bond low surface energy plastics such as Polupropylene, TPO, LDPE, HDPE, Teflon, PP, PE, PVC. Open time 2-3 min. and long cure speed 120-180min.
Size
50ml, 490ml, 18kg, 182kg
Mix Ratio
10 : 1
Colour
White
Min. Open Time [Minutes]
2
Max. Open Time [Minutes]
3
Min. Handling Strength [Minutes]
120
Max. Handling Strength [Minutes]
180
Max Gap Fill: [mm]
3
Approx Viscosity [cP]
8000
Shear Strength [psi] / [MPa] Alu / S.Steel/ Steel
1750
12
Min. Tensile Elongation (%)
5
Max. Tensile Elongation (%)
10
Temperature Range [˚C]
-55 ÷ 121

Primery i aktywatory

MC-2719
PR-MA
Structural Methacrylate Primer Red for 1:1 and 10:1 adhesives used on metals
Size
110ml, 1L
MC-2714
PR-MP
Primer for TPO, PP and tough to bond plasitics to use with MMA, PU and Epoxy adhesives.
Size
110ml, 1L
MC-2718
PRM
Primer for galvanized steel used with Structural Methacrylate and Cas
Size
1L
MC-2710
PR07
Polyolefin Primer fo CA, MMA
Size
50ml, 115ml, 1L

Końcówki miksujące, wyciskacze i akcesoria

MC-2721
GUN-50ml (1:1)
1:1, 50ml Grey Plastic Gun
MC-2724
GUN-400ml (1:1)
1:1 Cox 400ml Gun
MC-2728
GUN-490ml (10:1) - HD-MULTI RATIO
10:1 Heavy Duty Gun, multi ratio 10:1, 4:1, 2:1
MC-2723
GUN-490ml (10:1)
10:1 Standard Gun 490ml
MC-2722
GUN-50ml (10:1)
10:1 50ml Gun
MC-2725
Mixer Q 50ml
1:1 Green Quadro Mixing Nozzle 50ml
MC-2727
Mixer Q 400ml
1:1 Green Quadro Nozzle 400ml
MC-2726
Mixer 490ml 10:1
10:1 Mixing Nozzle 490ml
MC-2729
Mixer 50ml 10:1
10:1 Mixing Nozzle 50ml

Zmywacze

MC-6061
CLEAN-X
Dry cleaner and fast evaporating degreaser for surface preparation before bonding process. Compatible with plastics.
Size
600ml, 25l
MC-6060
CLEANER
Universal solvent cleaner, rapidly evaporating, cleaning and degreasing mechanical parts, electrical and electronic equipment.
Size
600ml, 25l
MC-6066
CLEAN-AP
Very strong, non-harmful, precision degreaser for chemical resistant surfaces. May harm plastics and coatings.
Size
25l
MC-1101M
CLEANER-NF
Vaery strong, nonflammable, dry solvent degreaser without chlorine based substances.
Size
600ml, 1kg, 25kg, 250kg
MC-9408M
MAXCLEAN
The strongest, nonflammable solvent degreaser, evaporates instantly. Disolves plastics.
Size
600ml, 1kg, 25kg, 250kg
MC-6065
BLUDET
"Safe, concentrated, multi-purpose cleaning agent and degreaser to use with water."
Size
5L, 25L